Technical
Specification |
|
1. |
Material |
100% Nitrile material.( Carboxylated
butadiene butadiene acrylonitrile
copolymer ) |
|
2. |
Glove
Features |
Ambidextrous.
Beaded cuff for enhance donning
Fast adapted to hand shape, comfort
and durable.
Textured surface for better feel and
grip.
Smooth surface for smooth feeling. |
|
3. |
Colour |
White, Blue and Translucent |
|
4. |
Glove
Specification |
ASTM D6319-00, Standard
Specification for Nitrile
Examination Gloves |
|
5. |
Quality Standards |
Manufactured according ISO9001-2000
Quality Management System. |
|
6. |
Quality Plan |
|
Parameter |
Inspection Level |
AQL |
| Liquid
Particles Count |
3
gloves from every batch,
approx 6,000 gloves |
Passed |
|
Extractable Contents |
1
glove from every batch,
approx 6,000 gloves |
Passed |
| Holes |
G 1 |
1.5 |
|
Dimension |
G 2 |
4.0 |
|
Tensile Properties |
G 2 |
4.0 |
| Visual
Defects-Major |
G 4 |
2.5 |
| Visual
Defects-Minor |
G 4 |
4.0 |
|
Major : Visible holes, Tear,
Excessive thin spots, Sticky
on inner/outer surfaces |
|
Minor : Non-removable dirts,
lumps, Defective bead,
Stain, Discolouration |
|
|
7. |
Technical properties |
Class 10 Specification |
Class 100 Specification |
|
Electrical Properties |
At 12.5% R. humidity |
At 12.5% R. humidity |
Resisitivity
(EST S11.12) |
1 x1011
ohms/square
At 50% R. humidity
1 x1010 ohms/square |
1 x1011
ohms/square
At 50% R. humidity
1 x1010 ohms/square |
|
With hand on |
At 50% R. humidity
1 x108 ohms/square |
At 50% R. humidity
1 x108 ohms/square |
Static Decay
(RETS-5-003)
(1000V - 10V) |
At 12.5% R. humidity
< 5 seconds
At 50% R. humidity
< 2 seconds |
At 12.5% R. humidity
< 3 seconds
At 50% R. humidity
< 2 seconds |
|
Total non-volatile residue |
1.5 ug/cm2 (IEST-RPCC005) |
2.5 ug/cm2 (IEST-RPCC005) |
Particles level (particles/cm2)
Ave.Total 0.5 - 20 um |
< 800 (IEST-RPcc005)
Orbital Shaker |
< 1,500 (IEST-RPcc005)
Orbital Shaker |
|
Extractable Contents (Ionic) |
Class 10 Specification |
Class 10 Specification |
Silicone
Amide
Phatalates
Fluoride (F-)
Chloride (Cl-)
Bromide (Br-)
Nitrate (NO3-)
Phosphate (PO43-)
Sulfate (SO42-)
Lithium (Li+)
Sodium (Na+)
Ammonium (NH4+)
Potassium ( K+ )
|Magnesium (Mg2+)
Calcium (Ca2+) |
None
None
None
< 0.0005 ug/cm2
< 0.100 ug/cm2
< 0.0005 ug/cm2
< 0.100 ug/cm2
< 0.005 ug/cm2
< 0.05 ug/cm2
< 0.0005 ug/cm2
< 0.050 ug/cm2
< 0.050 ug/cm2
< 0.050 ug/cm2
< 0.005 ug/cm2
< 0.050 ug/cm2 |
None
None
None
< 0.0005 ug/cm2
< 0.200 ug/cm2
< 0.0005 ug/cm2
< 0.200 ug/cm2
< 0.015 ug/cm2
< 0.05 ug/cm2
< 0.0010 ug/cm2
< 0.100 ug/cm2
< 0.100 ug/cm2
< 0.100 ug/cm2
< 0.010 ug/cm2
< 0.200 ug/cm2 |
|
8. |
Physical Dimension |
USEW77 |
|
Size |
XS |
S |
M |
L |
XL |
XXL |
|
Palm width, (+ - 5 mm) |
75 |
85 |
95 |
106 |
115 |
120 |
|
Weight, (+0.0g, -0.2g) |
6.7g |
6.9g |
7.7g |
8.5g |
9.1g |
10.1g |
|
Length, (+ - 10 mm) |
300mm / 12 inches |
Thickness, Single-wall
(+/- 0.02mm) |
|
|
Cuff |
0.10mm |
|
Palm |
0.14mm |
|
Finger-tips |
0.15mm |
|
9. |
Physical Properties |
Before ageing, Min |
After ageing, Min |
|
Tensile strength |
15 Mpa |
14 Mpa |
|
Elongation |
500% |
450% |
|
10. |
Packing & Marking |
Gloves are packed in a Class 10
cleanroom.
Polybags are cleanroom compatible,
easy opening and dust-free.
2 stages of 50 gloves vacuum-sealed
in 2 bags with cuffs aligned to the
opening edge.
10 bags per 2 liner polybags packed
in a shipping carton.
1,000 gloves per shipping carton.
Batch no and lot no printed on
packaging. |
|
11. |
Test
Report |
Each batch tested and documented.
Liquid Particles Count data
available upon request.
Chemicals extractable data available
upon request.
Chemical Compatibility Information
available upon request. |
Top
Nitrile
CR 300mm